Specification of Ordinary Portland Cement American Standard ASTM C 150 – TYPE 1
CHEMICAL COMPOSITIONS
CHEMICAL COMPOSITIONS | ||
---|---|---|
Loss on Ignition (LOI) % | 3.00 Max | 0.93 |
Insoluble Residue (I.R) % | 0.75 Max | 0.26 |
Silicon Oxide (SiO 2 ) % | 20.00 Min | 20.59 |
Aluminium Oxide (Al 2 O 3 ) % | 6.00 Max | 4.96 |
Iron Oxide (Fe 2 O 3 ) % | 6.00 Max | 3.77 |
Calcium Oxide (CaO) % | ----- | 63.35 |
Magnesium Oxide (MgO) % | 6.00 Max | 2.94 |
Sulphur Trioxide (SO 3 ) % | 3.00 Max | 1.96 |
Alkali Eq. | 0.60 | 0.53 |
C3S | ----- | 53.8 |
C2S | ----- | 20.19 |
C3A | 8.00 Max | 6.4 |
C4AF | ----- | 12.04 |
Chloride (Cl) | ----- | 0.01 |
PHYSICAL TEST
PHYSICAL TEST | ||
---|---|---|
Setting Time | ||
Initial Time (Min) | 60 Min | 105 |
Final Time (Min) | 600 Max | 350 |
Blaine (m 2 /kg) | 160 Min | 300 |
Expansion (%) | 0.80 Max | 0.04 |
Compressive Strength | ||
03 Days (PSI) | 1740 | 3948 |
07 Days (PSI) | 2760 | 5290 |
28 Days (PSI) | 4060 | 6400 |